PPO(PPE) VESTORAN® 1900GF20 Altuglas International of Arkema Inc.

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 179/1eA	12 kJ/m²
	Charpy Notched Impact Strength	0°C,Complete Break	ISO 179/1eA	12 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Complete Break	ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch	-30°C,Complete Break	ISO 179/1eU	50 kJ/m²
	Impact strength of simply supported beam without notch	0°C,Complete Break	ISO 179/1eU	50 kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C,Complete Break	ISO 179/1eU	50 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	29 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2	5600 MPa
tensile strength	Break	ISO 527-2	110 MPa
Tensile strain	Break	ISO 527-2	3.0 %
Bending modulus		ISO 178	5700 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	190 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	185 °C
Vicat softening temperature	--	ISO 306/A	200 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B	190 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD	ISO 294-4	0.60 %
Shrinkage rate	Shrinkage rate	MD:80°C,2.00mm	ISO 294-4	0.50 %
density		ISO 1183	1.19 g/cm³
Melt Volume Flow Rate (MVR)	300°C/21.6kg	ISO 1133	15.0 cm³/10min

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		IEC 60093	1E+13 ohms
Volume resistivity		IEC 60093	1E+13 ohms·cm
Dielectric strength		IEC 60243-1	33 kV/mm
Relative permittivity	100Hz	IEC 60250	2.90
Relative permittivity	Relative permittivity	1MHz	IEC 60250	2.70
Dissipation factor	100Hz	IEC 60250	8E-04
Dissipation factor	Dissipation factor	1MHz	IEC 60250	1.8E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA5	IEC 60112	PLC 3

Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون
ElectrolyticalCorrosion-Step		IEC 60426	A1
Relative WeldLineStrength		ISO 527	60 %