EHMWPE DuraSurf™ STS

مقایسه

برگه داده فنی

	شرایط آزمون	روش آزمون	نتیجه آزمون
Crystallinity	3.18mm	ASTM D3417	50 %
relative viscosity	762.0µm	ASTM D4020	230to350 cm³/g
Dissipation Factor	3.18mm,5MHz	ASTM D150	3.4E-03
tensile strength	屈服,3.18mm	ASTM D638	22.0 MPa
	tensile strength	断裂,0.762mm	ASTM D638	53.0 MPa
		tensile strength	断裂,1.52mm	ASTM D638	49.0 MPa
		tensile strength	tensile strength	断裂,3.18mm	ASTM D638	44.0 MPa
elongation	断裂,0.762mm	ASTM D638	60 %
	elongation	断裂,1.52mm	ASTM D638	460 %
	elongation	elongation	断裂,3.18mm	ASTM D638	470 %
coefficient of friction	与钢-动态3	ASTM D1894	0.10to0.22
	coefficient of friction	与钢-动态4	ASTM D1894	0.050to0.10
	coefficient of friction	coefficient of friction	与钢-动态5	ASTM D1894	0.050to0.080
StaticDecay	762.0µm		<10 msec
	StaticDecay	1.52mm		<10 msec
	StaticDecay	StaticDecay	3.18mm		<10 msec
Dissipation Factor	0.762mm,50Hz	ASTM D150	0.059
	Dissipation Factor	0.762mm,10kHz	ASTM D150	0.11
		Dissipation Factor	0.762mm,5MHz	ASTM D150	0.10
			Dissipation Factor	1.52mm,50Hz	ASTM D150	0.021
				Dissipation Factor	1.52mm,10kHz	ASTM D150	0.069
					Dissipation Factor	1.52mm,5MHz	ASTM D150	0.23
						Dissipation Factor	3.18mm,50Hz	ASTM D150	8.2E-03
						Dissipation Factor	Dissipation Factor	3.18mm,10kHz	ASTM D150	2.2E-03
Shore hardness	邵氏D,3.18mm	ASTM D2240	65
Tensile modulus	0.762mm	ASTM D638	725 MPa
	Tensile modulus	1.52mm	ASTM D638	731 MPa
	Tensile modulus	Tensile modulus	3.18mm	ASTM D638	672 MPa
tensile strength	屈服,0.762mm	ASTM D638	23.0 MPa
coefficient of friction	与自身-静态2	ASTM D1894	0.16
	coefficient of friction	与自身-静态6	ASTM D1894	0.16
	coefficient of friction	coefficient of friction	与自身-静态7	ASTM D1894	0.16
Impact strength of cantilever beam gap	3.18mm	ASTM D256	80 J/m
melting temperature	--6		134 °C
melting temperature	melting temperature	--2		136 °C
Linear coefficient of thermal expansion	MD：-100到-20°C,3.18mm	ASTM D696	9.2E-04 cm/cm/°C
dielectric constant	3.18mm	ASTM D150	2.54
coefficient of friction	与自身-动态2	ASTM D1894	0.14
	coefficient of friction	与自身-动态6	ASTM D1894	0.13
	coefficient of friction	coefficient of friction	与自身-动态7	ASTM D1894	0.14
relative viscosity	1.52mm	ASTM D4020	230to350 cm³/g
relative viscosity	relative viscosity	3.18mm	ASTM D4020	230to350 cm³/g
Shore hardness	邵氏D,0.762mm	ASTM D2240	65
Shore hardness	Shore hardness	邵氏D,1.52mm	ASTM D2240	65
tensile strength	屈服,1.52mm	ASTM D638	20.0 MPa
Linear coefficient of thermal expansion	MD：20到100°C,3.18mm	ASTM D696	1.5E-04 cm/cm/°C
Surface Resistivity	0.762mm	ASTM D257	1E+03 ohms
	Surface Resistivity	1.52mm	ASTM D257	1E+03 ohms
	Surface Resistivity	Surface Resistivity	3.18mm	ASTM D257	1E+03 ohms
Volume resistivity	0.762mm	ASTM D257	6E+07 ohms·cm
	Volume resistivity	1.52mm	ASTM D257	1.5E+07 ohms·cm
	Volume resistivity	Volume resistivity	3.18mm	ASTM D257	>2.0E+7 ohms·cm
dielectric strength	3.18mm	ASTM D149	14 kV/mm
dielectric constant	0.762mm	ASTM D150	2.48
dielectric constant	dielectric constant	1.52mm	ASTM D150	2.45
density		ASTM D792	0.930 g/cm³
Crystallinity	762.0µm	ASTM D3417	48 %
Crystallinity	Crystallinity	1.52mm	ASTM D3417	47 %