PC+PPC LEXAN™ 4251R resin

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.20 g/cm³
density	density		ISO 1183	1.10 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	5.6 g/10min
Melt volume flow rate	330°C/2.16kg	ISO 1133	31.4 cm³/10min
Shrinkage rate	MD：3.20mm	内部方法	0.60to0.80 %
Water absorption rate	饱和,23°C	ISO 62	0.24 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.090 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2/1	2160 MPa
tensile strength	Yield	ASTM D638	64.4 MPa
	tensile strength	Yield	ISO 527-2/50	62.6 MPa
		tensile strength	Break	ASTM D638	63.7 MPa
		tensile strength	tensile strength	Break	ISO 527-2/50	59.3 MPa
elongation	Yield	ASTM D638	6.7 %
Tensile strain	Yield	ISO 527-2/50	6.6 %
elongation	Break	ASTM D638	100 %
Tensile strain	Break	ISO 527-2/50	96 %
Flexural modulus	50.0mm跨距	ASTM D790	2230 MPa
Flexural modulus	Flexural modulus		ISO 178	2040 MPa
bending strength		ISO 178	7.50 MPa
bending strength	bending strength	屈服,50.0mm跨距	ASTM D790	101 MPa
Tensile modulus		ASTM D638	2180 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	48 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	330 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	640 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	21 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	44 kJ/m²
Dart impact	-30°C,TotalEnergy	ASTM D3763	78.1 J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	75.3 J

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat	--	ISO 306/B50	156 °C
vicat	vicat	--	ISO 306/B120	157 °C
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	6.2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40到40°C	ISO 11359-2	6.2E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	6.7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ISO 11359-2	6.7E-05 cm/cm/°C
Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	136 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,Unannealed,64.0mmSpan，HDT	ISO 75-2/Af	135 °C
vicat		ASTM D152510	156 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.