PP Teldene® B20ML National Petrochemical Industries Company (NATPET)

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-20°C	ISO 179/1e	4.0 kJ/m²
	Charpy Notched Impact Strength	0°C	ISO 179/1e	5.2 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1e	7.4 kJ/m²
Impact strength of simply supported beam without notch	-20°C	ISO 179/1eU	100 kJ/m²
	Impact strength of simply supported beam without notch	0°C	ISO 179/1eU	130 kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	23°C	ISO 180	6.5 kJ/m²

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Bending modulus		ISO 178	1600 MPa
Tensile modulus		ISO 527-2/1	1550 MPa
tensile strength	Yield	ISO 527-2/50	28.0 MPa
Tensile strain	Yield	ISO 527-2/50	5.0 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	>50 %

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	111 °C
Vicat softening temperature		ISO 306/A50	150 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density	23°C	ISO 1183	0.905 g/cm³
melt mass-flow rate	230°C/2.16kg	ASTM D1238	21 g/10min

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.