برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | TD | ASTM D955 | 0.60 % |
| Water absorption rate | Saturation | ASTM D570 | 0.15 % |
| density | | ASTM D792 | 1.18 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 0.60 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 850 °C |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 775 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 2500 MPa |
| tensile strength | Yield | ASTM D638 | 50.0 MPa |
| elongation | Break | ASTM D638 | >50 % |
| Flexural modulus | | ASTM D790 | 2700 MPa |
| bending strength | | ASTM D790 | 95.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 25 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 无断裂 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648A | 80.0 °C |
| vicat | | ASTM D15253 | 110 °C |
| RTI Elec | | UL 746 | 75.0 °C |
| RTI Imp | | UL 746 | 75.0 °C |
| RTI | | UL 746 | 75.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.