برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | | | 1.30 g/cm³ |
Water absorption rate | 23°C,24hr | ASTM D570 | 0.40 % |
hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Rockwell hardness | E计秤 | ASTM D785 | 104 |
Rockwell hardness | M-Scale | ASTM D785 | >125 |
Shore hardness | 邵氏D | ASTM D2240 | 95 |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Limiting Oxygen Index | | ASTM D2863 | 58 % |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
coefficient of friction | Steel - Dynamic | | 0.16 |
coefficient of friction | Steel - Static | | 0.15 |
coefficient of friction | 与金属-动态3 | | 0.16 |
coefficient of friction | 与金属-动态4 | | 0.18 |
coefficient of friction | 与金属-静态3 | | 0.14 |
coefficient of friction | 与金属-静态4 | | 0.16 |
bending strength | | ASTM D790 | 221 MPa |
Compression Modulus | | ASTM D695 | 5860 MPa |
compressive strength | --2 | ASTM D695 | 393 MPa |
compressive strength | 10%应变 | ASTM D695 | 345 MPa |
Tensile modulus | | ASTM D638 | 5860 MPa |
tensile strength | | ASTM D638 | 159 MPa |
elongation | Break | ASTM D638 | 3.0 % |
Fatigue-%ofstresstofailure | | ASTM D638 | 35 % |
Flexural modulus | | ASTM D790 | 6550 MPa |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 28 J/m |
Suspended wall beam without notch impact strength | | ASTM D256 | 590 J/m |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Volume resistivity | | ASTM D257 | 2E+15 ohms·cm |
dielectric strength | | ASTM D149 | 23 kV/mm |
dielectric constant | 1kHz | ASTM D150 | 3.40 |
dielectric constant | 10kHz | ASTM D150 | 3.40 |
dielectric constant | 100kHz | ASTM D150 | 3.30 |
Dissipation Factor | 1kHz | ASTM D150 | 0.0 |
Dissipation Factor | 10kHz | ASTM D150 | 3E-03 |
Dissipation Factor | 100kHz | ASTM D150 | 0.034 |
arc resistance | | ASTM D495 | 185 sec |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Linear coefficient of thermal expansion | MD:导热系数(25°C) | TMA | 0.40 W/m/K |
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 435 °C |
Glass Transition Temperature | | DMA | 427 °C |
Linear coefficient of thermal expansion | MD:24到149°C | TMA | 2.3E-05 cm/cm/°C |
Linear coefficient of thermal expansion | MD:199到299°C | TMA | 3.2E-05 cm/cm/°C |