| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | 23°C | ISO 1183 | 1.13 g/cm³ |
| melt mass-flow rate | 330°C/2.16 kg | ISO 1133 | 8.0 g/10 min |
| Melt volume flow rate | 330°C/2.16 kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | 横向流量 : 2.00 mm | ISO 294-4 | 0.90 % |
| Shrinkage rate | 流量 : 2.00 mm | ISO 294-4 | 0.90 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.30 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 130 Mpa |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ISO 489 | 1.566 |
| transmissivity | 1000 µm | ISO 13468-2 | 89.0 % |
| electrolytic corrosion | 23°C | IEC 60426 | A1 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 800 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2450 Mpa |
| tensile strength | 屈服, 23°C | ISO 527-2/50 | 76.0 Mpa |
| Tensile strain | 屈服, 23°C | ISO 527-2/50 | 6.9 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | > 50 % |
| Flexural modulus | 23°C | ISO 178 | 2450 Mpa |
| bending strength | 23°C | ISO 178 | 110 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+16 ohms |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+17 ohms·cm |
| dielectric strength | 23°C, 1.00 mm | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 23°C, 100 Hz | IEC 60250 | 2.90 |
| relative permittivity | 23°C, 1 MHz | IEC 60250 | 2.80 |
| Dissipation Factor | 23°C, 100 Hz | IEC 60250 | 1.0E-3 |
| Dissipation Factor | 23°C, 1 MHz | IEC 60250 | 9.0E-3 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | V |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 B | IEC 60112 | V |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Drying Temperature - Dry Air Dryer | | | 130 °C |
| Drying time - Dry Air Dryer | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | < 0.020 % |
| Suggested injection volume | | | 30 to 70 % |
| Temperature at the rear of the barrel | | | 315 to 325 °C |
| Temperature in the middle of the barrel | | | 320 to 330 °C |
| Temperature at the front of the material cylinder | | | 325 to 335 °C |
| Spray nozzle temperature | | | 315 to 340 °C |
| Processing (melt) temperature | | | 330 to 340 °C |
| Temperature | | | 110 to 150 °C |
| Back pressure | | | 10.0 to 20.0 Mpa |
| Exhaust hole depth | | | 0.025 to 0.050 mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 191 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 172 °C |
| vicat | | ISO 306/B120 | 202 °C |
| Linear coefficient of thermal expansion | 流动 : 23 到 55°C | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : 23 到 55°C | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 150 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI | | UL 746 | 150 °C |