PC/ABS A1225IR 6199
20
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5-0.7 % | |
| Water absorption rate | 23°C24h | ASTM D570 | 0.2 % |
| Yirong Index | 300℃ 1.2kg | ASTM D1238 | 20 g/10min |
| melt mass-flow rate | 300°C 1.2kg | ASTM D1238 | 19 cm3/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| transmissivity | 3000pm | ASTM D1003 | 89 % |
| Haze ratio | 3000pm | ASTM D1003 | 0.8 % |
| refractive index | ASTM D542 | 1.586 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | 1.0mm/min | ASTM D638 | 2300 Mpa |
| tensile strength | 50mnVmin，断裂 | ASTM D638 | 68 Mpa |
| 50mm/min，屈服 | ASTM D638 | 65 Mpa | |
| elongation | 50mm/min，屈服 | ASTM D638 | 6 % |
| elongation at break | 50mm/min | ASTM D638 | 120 % |
| Bending coverage | 2.0mm/min | ASTM D790 | 97 Mpa |
| Flexural modulus | 2.0mm/min | ASTM D790 | 2300 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 72 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa 3.2mm，HDT | ASTM D648 | 127 °C |
| vicat | 120℃/hr 50N | ASTM D1525 | 147 °C |