physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Apparent density | | JISK6891 | 1.00to1.40 g/cm³ |
melt mass-flow rate | 372°C/5.0kg | ASTM D1238 | 10to17 g/10min |
Water absorption rate | 饱和 | ASTM D570 | <0.010 % |
hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Shore hardness | 邵氏D | ASTM D2240 | 60to70 |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
UL flame retardant rating | 1.6mm | UL 94 | V-0 |
Limiting Oxygen Index | 1.57mm | ASTM D2863 | >95 % |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Heat distortion temperature | 25°C,14MPa3,HDT | ASTM D621 | 8.00to9.00 % |
Heat distortion temperature | 100°C,6.9MPa2,HDT | ASTM D621 | 2.00to3.00 % |
Heat distortion temperature | 100°C,6.9MPa3,HDT | ASTM D621 | 8.50to9.50 % |
bending strength | | ASTM D790 | Nobreak |
tensile strength | 屈服 | JISK6891 | 25.4to30.4 Mpa |
elongation | 断裂 | JISK6891 | 350to450 % |
Flexural modulus | | ASTM D790 | 580to690 Mpa |
Compression Modulus | | ASTM D695 | 490to590 Mpa |
compressive strength | 1%应变 | ASTM D695 | 4.90to5.90 Mpa |
compressive strength | 25%应变 | ASTM D695 | 31.4to33.3 Mpa |
compressive strength | 摩擦系数(与钢-静态) | ASTM D695 | 0.040to0.050 |
Heat distortion temperature | 25°C,14MPa2,HDT | ASTM D621 | 2.50to3.00 % |
Filling analysis | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
melt viscosity | 380°C | | 2.00E+6-2.50E+7 mPa·s |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
melting temperature | | ASTM D4591 | 300to310 °C |
Linear coefficient of thermal expansion | MD:20到100°C | ASTM D696 | 1.2E-04 cm/cm/°C |
specific heat | | | 1050 J/kg/°C |
thermal conductivity | | ASTMC177 | 0.26 W/m/K |
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.