PBT+PET SCHULADUR® A1 GF 30 HF FR 1
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ISO 1183/A | 1.68 g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 54.0 cm³/10min |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| burning rate | 0.750mm,Self-Extinguishing | ISO 3795 | 0.0 mm/min |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 675 °C |
| 3.0mm | IEC 60695-2-13 | 675 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 34 % | |
| burning rate | 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min | |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| 3.0mm | UL 94 | V-0 | |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| 3.0mm | IEC 60695-11-10,-20 | V-0 | |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 675 °C |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 kJ/m² |
| 23°C | ISO 179/1eU | 46 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 12000 MPa | |
| tensile strength | Break | ISO 527-2/1A/5 | 148 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 2.0 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/Af | 198 °C |
| vicat | -- | ISO 306/A50 | 218 °C |
| -- | ISO 306/B50 | 190 °C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 219 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.