optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
transmissivity	1000 μm	Internal Method	> 90.5	%
	transmissivity	2000 μm	Internal Method	> 90.0	%
		transmissivity	3000 μm	Internal Method	> 89.5	%
		transmissivity	transmissivity	6000 μm	ASTM D1003	> 88.0	%
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ASTM D4812	无断裂
	Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
		Suspended wall beam without notch impact strength	-30°C7	ISO 180/1U	130	kJ/m²
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C7	ISO 180/1U	130	kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	55.0	J
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	6.0 mm	UL 94	5VA
Burning wire flammability index	1.5 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	--2	ASTM D638	2370	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400	Mpa
tensile strength	Yield3	ASTM D638	64.0	Mpa
	tensile strength	Yield	ISO 527-2/50	64.0	Mpa
		tensile strength	Break3	ASTM D638	59.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	50.0	Mpa
elongation	Yield3	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break3	ASTM D638	72	%
		elongation	elongation	Break	ISO 527-2/50	52	%
Bending modulus	50.0 mm Span4	ASTM D790	2300	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2410	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	98.0	Mpa
injection	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			265 to 290	°C
Temperature in the middle of the barrel			275 to 300	°C
Temperature at the front of the material cylinder			290 to 310	°C
Spray nozzle temperature			280 to 305	°C
Processing (melt) temperature			290 to 310	°C
Mold temperature			70 to 95	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Be	131	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Ae	120	°C
Vicat softening temperature	--	ASTM D15259	137	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	139	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.1E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.4E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.1E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	8.0E-5	cm/cm/°C
RTI Elec		UL 746	115	°C
RTI Imp		UL 746	115	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	17.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.45 - 0.65	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.010	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dielectric constant	1.10 GHz	ASTM ES7-83	2.81
Dissipation factor	1.10 GHz	ASTM ES7-83	5.8E-3
Compared to the anti leakage trace index		UL 746	PLC 2