HIPS 9500
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Apparent density | ASTM D-792 | 0.59-0.64 g/cm3 | |
| melt mass-flow rate | 200℃/5.0kg | ASTM D-1238 | 3.5 g/10min |
| Shrinkage rate | MD，23℃ | ASTM D-955 | 0.40-0.70 % |
| density | ASTM D-792 | 1.04 g/cm3 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 60° | ASTM D-523 | 35 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | 23℃ | ASTM D-638 | 1930 MPa |
| tensile strength | 23℃，屈服 | ASTM D-638 | 18.0 MPa |
| elongation at break | 23℃ | ASTM D-638 | 45 % |
| Flexural modulus | 23℃ | ASTM D-790 | 1790 MPa |
| bending strength | 23℃ | ASTM D-790 | 38.0 MPa |
| Impact strength of cantilever beam gap | 23℃， 3.18mm | ASTM D-256 | 182 J/m |
| Rockwell hardness | ASTM D-785 | 44 L Scale |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| dielectric strength | 23℃，3.18mm | ASTM D-149 | 16 kV/mm |
| dielectric constant | 23℃， 1MHz | ASTM D-150 | 2.50 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000090 ℃ |
| Heat distortion temperature | 1.8MPa，退火，HDT | ASTM D-648 | 84.0 ℃ |
| vicat | ASTM D-1525 | 100 ℃ |