| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 23°C，60%RH | ASTM D570 | 0.22 % |
| melt mass-flow rate | | ASTM D1238 | 9 g/10min |
| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M刻度 | ASTM D785 | M80 |
| Shrinkage rate | //方向 | | 2 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| flammability | t0.8mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | 23°C | ASTM D790 | 91.5 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2650 Mpa |
| shearing strength | t2mm | ASTM D732 | 56 Mpa |
| tensile strength | 23°C | ASTM D638 | 62 Mpa |
| elongation | 23°C | ASTM D638 | 60 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | t3.2mm，缺口 | ASTM D256 | 6.5 kJ/m² |
| Impact strength of cantilever beam gap | t3.2mm | ASTM D1822 | 110 kgf·cm/cm² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melting temperature | 10°C/min | DSC | 165 °C |
| Thermal stability temperature | 0.46MPa | ASTM D648 | 158 °C |
| Thermal stability temperature | 1.86MPa | ASTM D648 | 110 °C |
| Linear coefficient of thermal expansion | 20°C-80°C | E831 | 13 *10 -5°C |