PP Copolymer PROTEQ™ C23UST4Z Ixom Operations Pty Ltd

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	280 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	580 J/m

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot filament ignition temperature	1.6mm	AS/NZS60695	550 °C
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Bending modulus	3.20mm	ASTM D790	1700 MPa
elongation	Break,3.20mm	ASTM D638	>150 %
tensile strength	3.20mm	ASTM D638	17.0 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD	ASTM D696	5.2E-05 cm/cm/°C
Vicat softening temperature		ASTM D15254	131 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	57.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	126 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD：3.00mm	ASTM D955	0.60 %
melt mass-flow rate	230°C/2.16kg	ASTM D1238	23 g/10min
density		ASTM D792	1.03 g/cm³

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	ShoreD,15Sec	ISO 868	59
Shore hardness	Shore hardness	ShoreD	ISO 868	66