TPE DGR 6185BK USA Advanced

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Permanent compression deformation	24°C,22hr	ISO 815	23	%
	Permanent compression deformation	100°C,22hr	ASTM D395	82	%
		Permanent compression deformation	70°C,22hr	ASTM D395	65	%
		Permanent compression deformation	Permanent compression deformation	24°C,22hr	ASTM D395	23	%
tear strength	24°C	ASTM D624	54.3	kN/m
tensile strength	100%Strain,23°C	ISO 37	10.1	MPa
tensile strength	tensile strength	Yield,23°C	ASTM D412	14.7	MPa
Permanent compression deformation	100°C,22hr	ISO 815	82	%
tensile strength	100%Strain,23°C	ASTM D412	10.1	MPa
Permanent compression deformation	70°C,22hr	ISO 815	65	%
tensile strength	Yield,23°C	ISO 37	14.7	MPa
elongation	Break,23°C	ASTM D412	260	%
elongation	elongation	Break,23°C	ISO 37	260	%
Stretch permanent deformation	100%Strain	ASTM D412	19	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D3389	160	mg
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Brittle temperature		ASTM D746	-51.1	°C
Brittle temperature	Brittle temperature		ISO 812	-51.1	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD：1.59mm		1.9	%
density		ISO 2781	1.14	g/cm³
density	density		ASTM D471	1.14	g/cm³
MeltViscosity	190°C,300sec^-1	ASTM D3835	1060	Pa·s
Shrinkage rate	MD：3.18mm		1.2	%
	Shrinkage rate	TD：1.59mm		1.0	%
	Shrinkage rate	Shrinkage rate	TD：3.18mm		0.80	%
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	ShoreA,5Sec	ASTM D2240	85
Shore hardness	Shore hardness	ShoreA,5Sec	ISO 48	85
aging	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume change	70°C,168hr,inIRM903Oil	ASTM D471	130	%
	Volume change	24°C,168hr,inReferenceFuelB	ISO 1817	87	%
	Volume change	Volume change	70°C,168hr,inWater	ASTM D471	1.0	%
Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	-6.0	%
	Change rate of tensile strength in air	100°C,168hr	ASTM D573	-19	%
		Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	-4.0	%
		Change rate of tensile strength in air	Change rate of tensile strength in air	70°C,168hr	ISO 188	-16	%
Volume change	70°C,168hr,inASTM#1Oil	ASTM D471	27	%
Volume change	Volume change	24°C,168hr,inReferenceFuelB	ASTM D471	87	%
Tensile stress change rate	100°C,168hr，Break	ISO 188	-21	%
Tensile stress change rate	Tensile stress change rate	70°C,168hr，Break	ISO 188	-15	%
Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	-21	%
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	-15	%
Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	-6.0	%
Change rate of tensile strength in air	Change rate of tensile strength in air	100°C,168hr	ISO 188	-19	%
Volume change	70°C,168hr,inASTM#1Oil	ISO 1817	27	%
	Volume change	70°C,168hr,inIRM903Oil	ISO 1817	130	%
	Volume change	Volume change	70°C,168hr,inWater	ISO 1817	1.0	%
Change rate of tensile strength in air	70°C,168hr	ASTM D573	-16	%
Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	-4.0	%

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.