Fluorelastomer Viton® F-605C
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.90 g/cm³ | |
| Mooney viscosity | ML1+10,121°C | ASTM D1646 | 60 MU |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | 邵氏A,23°C2 | ASTM D2240 | 67 |
| 邵氏A,23°C3 | ASTM D2240 | 77 | |
| 邵氏A,23°C4 | ASTM D2240 | 76 |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| compression set | 200°C,22hr | ASTM D395B | 18 % |
| 200°C,70hr | ASTM D395B | 30 % | |
| tensile strength | 100%应变,23°C5 | ASTM D412 | 4.10 MPa |
| 100%应变,23°C6 | ASTM D412 | 6.10 MPa | |
| 100%应变,23°C7 | ASTM D412 | 5.80 MPa | |
| 屈服,23°C5 | ASTM D412 | 10.8 MPa | |
| 屈服,23°C6 | ASTM D412 | 14.9 MPa | |
| 屈服,23°C7 | ASTM D412 | 14.6 MPa | |
| elongation | 断裂,23°C5 | ASTM D412 | 280 % |
| 断裂,23°C6 | ASTM D412 | 250 % | |
| 断裂,23°C7 | ASTM D412 | 210 % | |
| compression set | 150°C,70hr | ASTM D395B | 14 % |
| aging | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| volume change | FuelC/Methanol85/15 | ASTM D471 | 9.0 % |