PC LNP™ LUBRICOMP™ DFL32XXP compound SABIC
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.67 % |
| MD：24小时 | ASTM D955 | 0.20 % | |
| density | ASTM D792 | 1.37 g/cm³ | |
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.23 % |
| TD：24hr | ASTM D955 | 0.70 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.11 % |
| 平衡,23°C,50%RH | ISO 62 | 0.18 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Break | ISO 527-2 | 71.0 MPa |
| Flexural modulus | ISO 178 | 4170 MPa | |
| ASTM D790 | 4350 MPa | ||
| bending strength | ASTM D790 | 124 MPa | |
| Tensile strain | Break | ISO 527-2 | 2.8 % |
| elongation | Break | ASTM D638 | 3.1 % |
| tensile strength | Break | ASTM D638 | 73.4 MPa |
| Tensile modulus | ASTM D638 | 4350 MPa | |
| ISO 527-2/1 | 4290 MPa | ||
| bending strength | ISO 178 | 114 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 11.6 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.29 J | |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 530 J/m |
| 23°C | ISO 180/1A | 10 kJ/m² | |
| 23°C | ASTM D256 | 91 J/m | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 141 °C |
| 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 140 °C |