physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | | ASTM D792 | 1.05 g/cm³ |
density | | ISO 1183 | 1.04 g/cm³ |
melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 40 g/10min |
Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
Water absorption rate | 23°C,24hr | ASTM D570 | 0.30 % |
hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Rockwell hardness | R级 | ASTM D785 | 114 |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
UL flame retardant rating | | UL 94 | HB |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Flexural modulus | | ASTM D790 | 2300 Mpa |
bending strength | | ASTM D790 | 73.0 Mpa |
bending strength | | ISO 178 | 77.0 Mpa |
Tensile modulus | | ISO 527-2/1 | 2600 Mpa |
tensile strength | 屈服 | ASTM D638 | 46.0 Mpa |
tensile strength | 屈服 | ISO 527-2/50 | 51.0 Mpa |
elongation | 断裂 | ASTM D638 | 15 % |
Tensile strain | 断裂 | ISO 527-2/50 | >10 % |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 18 kJ/m² |
Impact strength of cantilever beam gap | -30°C,3.20mm | ASTM D256 | 110 J/m |
Impact strength of cantilever beam gap | -30°C,12.7mm | ASTM D256 | 80 J/m |
Impact strength of cantilever beam gap | 0°C,3.20mm | ASTM D256 | 160 J/m |
Impact strength of cantilever beam gap | 0°C,12.7mm | ASTM D256 | 110 J/m |
Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 220 J/m |
Impact strength of cantilever beam gap | 23°C,12.7mm | ASTM D256 | 200 J/m |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Surface Resistivity | | ASTM D257 | >1.0E+16 ohms |
Volume resistivity | 23°C | ASTM D257 | >1.0E+16 ohms·cm |
dielectric strength | | ASTM D149 | 23 KV/mm |
dielectric constant | 1kHz | ASTM D150 | 3.10 |
Dissipation Factor | 1kHz | ASTM D150 | 6.2E-03 |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Heat distortion temperature | 1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 86.0 °C |
Heat distortion temperature | 1.8MPa,未退火,12.7mm,HDT | ASTM D648 | 92.0 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 81.0 °C |
Linear coefficient of thermal expansion | MD | ASTM D696 | 7.2E-05 cm/cm/°C |
thermal conductivity | | ASTMC177 | 0.16 W/m/K |