ABS HM42 TYNE USA
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.04 g/cm3 | |
| Shrinkage rate | MD | ASTM D955 | 0.60-0.80 % |
| density | ASTM D792 | 1.04 g/cm³ | |
| Shrinkage rate | MD | ASTM D995 | 0.60-0.80 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 100 R |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 100 R 计秤 | |
| elongation at yield | ASTM D638 | 42.7 % | |
| Flexural modulus | ASTM D790 | 2210 MPa | |
| bending strength | ASTM D790 | 68.9 MPa | |
| Impact strength of cantilever beam gap | 3.18mm | ASTM D256 | 220 J/m |
| bending strength | 23°C | ASTM D790 | 68.90 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2210 MPa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 220 J/m |
| Flame retardant performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 3.18mm | |
| UL -94 | HB 1.59mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 97.8 ℃ |
| UL flame retardant rating | 1.59mm | UL 94 | HB |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 97.80 °C |