MPR 2360 NC USA Advanced

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.12 g/cm³
density	density		ISO 1183	1.12 g/cm³
Apparent viscosity	190°C,300sec^-1	ASTM D3835	170 Pa·s

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	Shore A	ASTM D2240	61
Shore hardness	Shore hardness	Shore A	ISO 868	61

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Taber abraser	1000g,CS-17Wheel	ASTM D1044	0.0310 mg
Taber abraser	Taber abraser	1000g,CS-18Wheel	ASTM D1044	0.333 mg

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
compression set	24°C,22hr	ISO 815	16 %
	compression set	70°C,22hr	ISO 815	52 %
	compression set	compression set	100°C,22hr	ISO 815	66 %
Stretch permanent deformation		ASTM D412	9 %
tensile strength	100%应变	ASTM D412	2.55 MPa
	tensile strength	100%应变	ISO 37	2.55 MPa
		tensile strength	Yield	ASTM D412	8.27 MPa
		tensile strength	tensile strength	Yield	ISO 37	8.27 MPa
elongation	Break	ASTM D412	380 %
elongation	elongation	Break	ISO 37	380 %
tear strength	24°C	ASTM D624	24.5 kN/m
tear strength	tear strength	24°C	ISO 34-1	25 kN/m
compression set	24°C,22hr	ASTM D395A	16 %
	compression set	70°C,22hr	ASTM D395A	52 %
	compression set	compression set	100°C,22hr	ASTM D395A	66 %

aging	شرایط آزمون	روش آزمون	نتیجه آزمون
volume change	100°C,168hr,inASTM#1Oil	ASTM D471	-28 %
	volume change	100°C,168hr,inIRM903Oil#3	ASTM D471	-19 %
		volume change	100°C,168hr,在水中	ASTM D471	-43 %
			volume change	100°C,168hr,inASTM#1Oil	ISO 1817	-28 %
				volume change	100°C,168hr,在水中	ISO 1817	-43 %
				volume change	volume change	100°C,56640hr,inIRM903Oil#3	ISO 1817	-19 %
Change rate of tensile strength in air	125°C,168hr	ASTM D573	130 %
	Change rate of tensile strength in air	100%Strain,125°C,168hr	ASTM D573	110 %
		Change rate of tensile strength in air	125°C,168hr	ISO 188	130 %
		Change rate of tensile strength in air	Change rate of tensile strength in air	100%应变125°C,168hr	ISO 188	110 %
elongation at break	125°C,168hr	ASTM D573	96 %
Change rate of ultimate elongation in air	125°C,168hr	ISO 188	96 %

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
brittle temperature		ASTM D746	-41.0 °C
brittle temperature	brittle temperature		ISO 812	-41.0 °C