برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 337°C/6.6 kg | ASTM D1238 | 18 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.25 % |
| Water absorption rate | 平衡, 23°C | ASTM D570 | 1.3 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M 级 | ASTM D785 | 109 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| Limiting Oxygen Index | | ASTM D2863 | 44 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 3580 Mpa |
| tensile strength | 屈服 | ASTM D638 | 110 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| elongation | 断裂 | ASTM D638 | 60 % |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 3510 Mpa |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 165 Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1300 J/m |
| Reverse notch impact | 3.20 mm | ASTM D256 | 1500 J/m |
| Dart impact | 23°C | ASTM D3029 | 33.0 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 1.0E+17 ohms·cm |
| dielectric strength | 1.60 mm, in Air | ASTM D149 | 33 KV/mm |
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 28 KV/mm |
| dielectric constant | 1 kHz | ASTM D150 | 3.15 |
| Dissipation Factor | 1 kHz | ASTM D150 | 1.3E-3 |
| Dissipation Factor | 2.45 GHz | ASTM D150 | 2.5E-3 |
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| High arc combustion index (HAI) | | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | | UL 746 | PLC 1 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 150 °C |
| drying time | | | 4.0 to 6.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 40 to 60 % |
| Temperature at the rear of the barrel | | | 330 to 400 °C |
| Temperature in the middle of the barrel | | | 340 to 400 °C |
| Temperature at the front of the material cylinder | | | 345 to 400 °C |
| Spray nozzle temperature | | | 345 to 400 °C |
| Processing (melt) temperature | | | 350 to 400 °C |
| Temperature | | | 135 to 165 °C |
| Back pressure | | | 0.300 to 0.700 Mpa |
| screw speed | | | 40 to 70 rpm |
| Exhaust hole depth | | | 0.025 to 0.076 mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 207 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 198 °C |
| vicat | | ASTM D15255 | 218 °C |
| Linear coefficient of thermal expansion | -20 到 150°C，流动 | ASTM E831 | 5.6E-5 cm/cm/°C |
| thermal conductivity | | ASTM C177 | 0.22 W/m/K |
| RTI Elec | | UL 746 | 170 °C |
| RTI Imp | | UL 746 | 170 °C |
| RTI | | UL 746 | 170 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه
مشاهده قیمت‌ها