impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.0	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	77.0	J
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ASTM D638	2150	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2300	Mpa
bending strength		ISO 178	92.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	95.0	Mpa
tensile strength	Yield	ASTM D638	60.0	Mpa
	tensile strength	Yield	ISO 527-2/50	60.0	Mpa
		tensile strength	Break	ASTM D638	63.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	62.0	Mpa
elongation	Yield	ASTM D638	6.3	%
Tensile strain	Yield	ISO 527-2/50	5.8	%
elongation	Break	ASTM D638	140	%
Tensile strain	Break	ISO 527-2/50	130	%
Bending modulus	50.0mmSpan	ASTM D790	2300	Mpa
Bending modulus	Bending modulus		ISO 178	2260	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	TD：23to60°C	ISO 11359-2	9E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	106	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	108	°C
Vicat softening temperature		ASTM D152511	126	°C
	Vicat softening temperature	--	ISO 306/B50	125	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	126	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	6.8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：23to60°C	ISO 11359-2	9E-05	cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1E-04	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6.8E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	119	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	106	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	265°C/2.16kg	ASTM D1238	12	g/10min
Melt Volume Flow Rate (MVR)	265°C/2.16kg	ISO 1133	11.5	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60	%
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.50-0.70	%
Water absorption rate	Saturation,23°C	ISO 62	0.12	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.050	%