| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| characteristic | | | 注射成型 |
| purpose | | | 高速注射. 容器 |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | | ASTM D-1238 | 33 g/10min |
| density | | ASTM D-1505 | 0.950 g/cm |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 2 kg·cm/cm(J/M)ft·lb/in |
| Flexural modulus | | ASTM D790/ISO 178 | 8500 kg/cm²(MPa)[Lb/in²] |
| tensile strength | 断裂 | ASTM D-638 | 70 kg/cm |
| tensile strength | 屈服 | ASTM D-638 | 230 kg/cm |
| elongation | 断裂 | ASTM D-638 | 270 % |
| Impact strength of cantilever beam gap | | ASTM D-256 | 2 kg.cm/cm |
| bending strength | | ASTM D-747 | 8500 kg/cm |
| Shore hardness | | ASTM D-2240 | 61 Shore D |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Environmental stress cracking resistance | | ASTM D-1693 | 2 hr |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792/ISO 1183 | 0.95 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 45 g/10min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D1525/ISO R306 | 122 ℃（℉） |
| melting temperature | | ASTM D-2117 | 130 °C |
| vicat | | ASTM D-1525 | 122 °C |