برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 23°C,24hr | ISO 62 | <0.10 % |
| Shrinkage rate | | ISO 2577 | <0.050 % |
| Shrinkage rate | MD | ISO 2577 | 0.40to0.60 % |
| density | | ISO 1183 | 1.93to1.98 g/cm³ |
| Apparent density | | ISO 60 | 0.80to0.90 g/cm³ |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 900 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 900 °C |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compression molding pressure | | | >5.00 MPa |
| Compression molding temperature | | | 150to190 °C |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.0to4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 12to14 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 15000to18000 MPa |
| tensile strength | | ISO 527-2 | 70.0to90.0 MPa |
| Flexural modulus | | ISO 178 | 15000to20000 MPa |
| bending strength | | ISO 178 | 140to160 MPa |
| compression stress | | ISO 604 | 200to250 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+13到1.0E+14 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 25to35 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 5.007.00 |
| relative permittivity | 1MHz | IEC 60250 | 4.006.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.030to0.050 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010to0.030 |
| arc resistance | | ASTM D495 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 160to180 °C |
| Linear coefficient of thermal expansion | MD：50到150°C | ISO 11359-2 | 1.5E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40to0.60 W/m/K |
| maximum service temperature | <50h | IEC 60216 | 250 °C |
| maximum service temperature | 20,000h | IEC 60216 | 180 °C |