برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.21 g/cm³ |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 9.0to16 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| Shrinkage rate | TD：3.18mm | ASTM D955 | 0.50to0.70 % |
| Outdoor applicability | | UL 746C | f1 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | 3.18mm | ASTM D790 | 89.6 MPa |
| elongation | 屈服,3.18mm | ASTM D638 | 7.0 % |
| tensile strength | 屈服,3.17mm | ASTM D638 | 62.1 MPa |
| tensile strength | Break,3.18mm | ASTM D638 | 55.2 MPa |
| elongation | 断裂,3.18mm | ASTM D638 | 90 % |
| Flexural modulus | 3.17mm | ASTM D790 | 2210 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 640 J/m |
| Dart impact | 3.18mm | ASTM D3029 | >36.2 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | 1.50mm | ASTM D149 | 23 kV/mm |
| arc resistance | 1.50mm | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | 1.50mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| Volume resistivity | | ASTM D257 | 1E+17 ohms·cm |
| High Voltage Arc Traceability Rate (HVTR) | 1.50mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI Imp | 3.0mm | UL 746 | 110 °C |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| RTI Str | 3.0mm | UL 746 | 125 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 129 °C |
| vicat | | ASTM D15252 | 149 °C |
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| RTI Elec | 3.0mm | UL 746 | 125 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 135 °C |
| RTI Imp | 1.5mm | UL 746 | 110 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.