PP GLS PP ZT89 GLS Polymers Pvt. Ltd.
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.22to1.24 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | >5.0 g/10min |
| 230°C/2.16kg | ASTM D1238 | >5.0 g/10min | |
| density | ASTM D792 | 1.22to1.24 g/cm³ |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 3000to3400 MPa | |
| bending strength | ASTM D790 | 45.0to50.0 MPa | |
| tensile strength | ASTM D638 | 30.0to34.0 MPa | |
| elongation | Break | ASTM D638 | >10 % |
| tensile strength | ASTM D638 | 30.0to34.0 MPa | |
| elongation | Break | ASTM D638 | >10 % |
| Flexural modulus | ASTM D790 | 3000to3400 MPa | |
| bending strength | ASTM D790 | 45.0to50.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 30to40 J/m |
| 3.20mm | ASTM D256 | 30to40 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 78.0to82.0 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 78.0to82.0 °C |