PA6 Staramide BST44 EUROSTAR FRANCE

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	23°C	ISO 179/1eA	75	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	60	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	>100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	>100	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	50	kJ/m²
	Impact strength of cantilever beam gap	-20°C	ISO 180/1A	65	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	75	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Yield	ISO 527-2/50	50.0	MPa
Tensile modulus		ISO 527-2/1	1900	MPa
elongation	Yield2	ASTM D638	4.1	%
bending strength		ISO 178	60.0	MPa
Bending modulus		ISO 178	1600	MPa
elongation	Break	ISO 527-2/50	>100	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	9.5E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	160	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	165	°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	60.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	140	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0	%
density		ISO 1183	1.08	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	--	IEC 60112	PLC 1
Dissipation factor	1MHz	IEC 60250	0.017
	Dissipation factor	60Hz	IEC 60250	8.4E-03
	Dissipation factor	Dissipation factor	50Hz	IEC 60250	8.4E-03
Relative permittivity	1MHz	IEC 60250	2.80
Relative permittivity	Relative permittivity	60Hz	IEC 60250	3.00
Surface resistivity		IEC 60093	>1.0E+16	ohms
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Dielectric strength	3.20mm,in Oil	IEC 60243-1	16	kV/mm
Relative permittivity	50Hz	IEC 60250	3.00
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Sale	ISO 2039-2	111