MDPE Marlex® K307 Chevron Phillips Chemical Company LLC
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Environmental stress cracking resistance | 100%Igepal,模压成型,F50 | ASTM D1693C | >1500 hr |
| SP-NCTL | ASTM D5397 | >1.2 month | |
| density | ASTM D1505 | 0.937 g/cm³ | |
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 21 g/10min |
| Environmental stress cracking resistance | 10%Igepal,模压成型,F50 | ASTM D1693B | >1500 hr |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | 邵氏D,模压成型 | ASTM D2240 | 57 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Yield,CompressionMolded | ASTM D638 | 20.0 MPa |
| Tensile strain | Break,CompressionMolded | ASTM D638 | 800 % |
| Flexural modulus | CompressionMolded，正切 | ASTM D790 | 830 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact Strength | CompressionMolded | ASTM D1822 | 400 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,模压成型，HDT | ASTM D648 | 58.0 °C |
| brittle temperature | ASTM D746A | <-75.0 °C | |
| vicat | ASTM D15257 | 105 °C |