ABS MALECCA K-095 DENKA JAPAN
111
- ویژگی‌ها:مقاوم در برابر گرما
مقایسه
مشاهده قیمتهابرگه داده فنی
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 220℃,10kg | JIS K-6874 | 10 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 78 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 42 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 114 | |
| Flexural modulus | ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 74 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 206 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | 15mm/min | ASTM D-790 | 74 Mpa |
| Rockwell hardness | 23℃ | ASTM D-785 | 114 R |
| tensile strength | ASTM D-638 | 42 Mpa | |
| Impact strength of cantilever beam gap | 1/4＂带缺口23℃ | ASTM D-256 | 206 J/m |
| Flexural modulus | 15mm/min | ASTM D-790 | 2350 Mpa |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| Shrinkage rate | ASTM D955 | 0.4-0.6 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 100 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 110 ℃（℉） | |
| 5kg | JIS K-7206 | 110 °C | |
| Heat distortion temperature | 6.4mm,1.82MPa，HDT | ASTM D-648 | 100 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.