EPE 5101G
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.85 g/10min |
| density | ASTM D792 | 0.922 g/cm³ |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 45°,50.8µm | ASTM D2457 | 58 |
| Haze ratio | 50.8µm | ASTM D1003 | 15 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| film thickness | 51 µm | ||
| Thin film puncture strength | 51µm | 内部方法 | 4.29 J |
| 51µm | 内部方法 | 71.2 N | |
| 51µm | 内部方法 | 11.0 J/cm³ | |
| Secant modulus | 2%正割,MD:51µm | ASTM D882 | 219 MPa |
| 2%正割,TD:51µm | ASTM D882 | 248 MPa | |
| tensile strength | MD:屈服,51µm | ASTM D882 | 9.79 MPa |
| TD:屈服,51µm | ASTM D882 | 11.0 MPa | |
| MD:断裂,51µm | ASTM D882 | 40.8 MPa | |
| TD:断裂,51µm | ASTM D882 | 38.4 MPa | |
| elongation | MD:断裂,51µm | ASTM D882 | 590 % |
| TD:断裂,51µm | ASTM D882 | 620 % | |
| Dart impact | 51µm | ASTM D1709B | >850 g |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 720 g |
| TD:51µm | ASTM D1922 | 1000 g | |
| Initial sealing temperature | 51µm | 内部方法 | 106 °C |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | ASTM D1525 | 105 °C | |
| melting temperature | 内部方法 | 121 °C |