Copolyester GS1 Eastman Chemical Company

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density	--2	ASTM D1505	1.27 g/cm³
density	density	--	ASTM D1505	1.28 g/cm³
Water absorption rate	23°C,24hr	ASTM D570	0.16 %
intrinsic viscosity	23°C	内部方法	0.71
intrinsic viscosity	intrinsic viscosity	Pellets:23°C	内部方法	0.75

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
gloss	60°,170µm	ASTM D2457	107
transmissivity	总计,170µm	ASTM D1003	90.0 %
Haze ratio	170µm	ASTM D1003	2.7 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Limiting Oxygen Index		ASTM D2863	24 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dart impact	-20°C,EnergyatPeakLoad	ASTM D3763	0.700 J
	Dart impact	0°C,EnergyatPeakLoad	ASTM D3763	1.20 J
	Dart impact	Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	1.60 J

film	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	TD:屈服,170µm	ASTM D882	5.0 %
	elongation	MD:断裂,170µm	ASTM D882	420 %
	elongation	elongation	TD:断裂,170µm	ASTM D882	300 %
Elmendorf tear strength	MD:170µm	ASTM D1922	730 g
Elmendorf tear strength	Elmendorf tear strength	TD:170µm	ASTM D1922	900 g
OTr	23°C,170µm,50%RH	ASTM D3985	7.0 cm³·mm/m²/atm/24hr
Water Vapor Transmission Rate	38°C,100%RH,170µm	ASTMF372	7.0 g/m²/24hr
tensile strength	MD:断裂,170µm	ASTM D882	63.0 MPa
tensile strength	tensile strength	TD:断裂,170µm	ASTM D882	46.0 MPa
elongation	MD:屈服,170µm	ASTM D882	5.0 %
film thickness			170 µm
Secant modulus	MD:170µm	ASTM D882	1600 MPa
Secant modulus	Secant modulus	TD:170µm	ASTM D882	1600 MPa
tensile strength	MD:屈服,170µm	ASTM D882	49.0 MPa
tensile strength	tensile strength	TD:屈服,170µm	ASTM D882	49.0 MPa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
dielectric strength	23°C	ASTM D149	15 kV/mm
dielectric constant	23°C,1kHz	ASTM D150	2.88
dielectric constant	dielectric constant	23°C,1MHz	ASTM D150	2.68
Dissipation Factor	23°C,1kHz	ASTM D150	0.022
Dissipation Factor	Dissipation Factor	23°C,1MHz	ASTM D150	0.021
arc resistance		ASTM D495	131 sec
Surface Resistivity		ASTM D257	1.2E+16 ohms
Volume resistivity	23°C	ASTM D257	3.9E+16 ohms·cm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD：23°C	ASTM D696	7.7E-05 cm/cm/°C
specific heat	23°C	DSC	1300 J/kg/°C
	specific heat	100°C	DSC	1700 J/kg/°C
		specific heat	150°C	DSC	1800 J/kg/°C
			specific heat	200°C	DSC	2000 J/kg/°C
			specific heat	specific heat	250°C	DSC	2100 J/kg/°C
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648	70.0 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ASTM D648	62.0 °C
Glass Transition Temperature		DSC	81.0 °C
vicat		ASTM D1525	81.0 °C