ABS/PC CYCOLOY™ XCY630L-BK1566U SABIC INNOVATIVE US
548
مقایسه
مشاهده قیمتهابرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 26 g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 22.0 cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| TD：3.20mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % | |
| MeltViscosity | 260°C,1500sec^-1 | ISO 11443 | 170 Pa·s |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2300 Mpa | |
| ISO 527-2/1 | 2250 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 54.0 Mpa |
| elongation | 屈服 | ASTM D638 | 4.5 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.5 % |
| elongation | 断裂 | ASTM D638 | 120 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2300 Mpa |
| ISO 178 | 2200 Mpa | ||
| bending strength | ISO 178 | 82.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 89.0 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 54.0 Mpa |
| 断裂 | ASTM D638 | 53.0 Mpa | |
| 断裂 | ISO 527-2/50 | 53.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 30 kJ/m² |
| 23°C | ISO 179/1eA | 65 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 30 kJ/m² |
| 23°C | ISO 180/1A | 65 kJ/m² | |
| Dart impact | -30°C,TotalEnergy | ASTM D3763 | 67.0 J |
| 23°C,TotalEnergy | ASTM D3763 | 55.0 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm | |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | -- | ISO 306/B50 | 126 °C |
| -- | ISO 306/B120 | 127 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 126 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 107 °C | |
| 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 105 °C | |
| vicat | ASTM D152510 | 126 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K |