برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | Saturation | ISO 622 | 0.030 % |
| Water absorption rate | Equilibrium | ISO 622 | 0.23 % |
| density | | ISO 1183/A | 1.20 g/cm³ |
| density | | ISO 11832 | 1200 kg/m³ |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 15 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 11332 | 12.0 cm³/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.50to0.70 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-2 |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| Burning Behav. | 1.60mm,UL | ISO 12102 | V-2 |
| Burning Behav.atthicknessh | 3.20mm,UL | ISO 12102 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/50 | 2300 MPa |
| Tensile modulus | | ISO 527-22 | 2300 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| tensile strength | Yield | ISO 527-22 | 60.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 66.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 % |
| Tensile strain | Yield | ISO 527-22 | 6.0 % |
| Tensile strain | Break | ISO 527-2/50 | 120 % |
| Nominal fracture strain | | ISO 527-22 | >50 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 100 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | 17.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA2 | 15.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eU2 | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 83 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | 2.00mm,SolutionA | IEC 60112 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 601122 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 122 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 139 °C |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 122 °C |
| vicat | | ISO 306/B50 | 147 °C |
| vicat | 50N | ISO 3062 | 147 °C |
| Ball pressure temperature | | IEC 60335-1 | 125 °C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 142 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-22 | 140 °C |