other	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
characteristic			注射级.30%玻纤
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength		ASTM D256/ISO 179	13	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	10	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	70	kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap		ASTM D256/ISO 179	55	kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap		ASTM D256/ISO 179	15	kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	10	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	3	%
Tensile modulus		ASTM D638/ISO 527	9900	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	180	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	8300	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	280	kg/cm²(MPa)[Lb/in²]
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	HDT	ASTM D648/ISO 75	-200	℃（℉）
Melting temperature			222	℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	>200	℃（℉）
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate		ASTM D955	0.17	%