برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Specific volume | | ASTM D792 | 0.835 cm³/g |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 2.0 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 2.00 cm³/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.80to1.0 % |
| saturation | | ISO 62 | 0.16 % |
| balance | | ISO 62 | 0.35 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 92 |
| Rockwell hardness | R-Scale | ASTM D785 | 127 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| refractive index | | ASTM D542 | 1.600 |
| transmissivity | 2540µm | ASTM D1003 | 85.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.47mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| yield | | ASTM D790 | 97.2 MPa |
| yield | | ASTM D638 | 65.5 MPa |
| yield | | ISO 527-2/50 | 68.0 MPa |
| fracture | | ASTM D638 | 77.9 MPa |
| fracture | | ISO 527-2/50 | 68.0 MPa |
| yield | | ASTM D638 | 8.0 % |
| yield | | ISO 527-2/50 | 7.0 % |
| fracture | | ASTM D638 | 78 % |
| fracture | | ISO 527-2/50 | 100 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 74.0 J |
| Dart impact | 23°C | ASTM D3029 | 149 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 578 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | >2.5E+17 ohms·cm |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 20 kV/mm |
| dielectric constant | 50Hz | ASTM D150 | 3.27 |
| dielectric constant | 60Hz | ASTM D150 | 3.27 |
| dielectric constant | 1MHz | ASTM D150 | 3.10 |
| Dissipation Factor | 50Hz | ASTM D150 | 1.6E-03 |
| Dissipation Factor | 60Hz | ASTM D150 | 1.6E-03 |
| Dissipation Factor | 100Hz | ASTM D150 | 0.026 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| thermal conductivity | | ASTMC177 | 0.21 W/m/K |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI | | UL 746 | 130 °C |
| specific heat | | ASTMC351 | 1260 J/kg/°C |
| flow | | ASTME831 | 6E-05 cm/cm/°C |
| flow | | ASTME831 | 8.1E-05 cm/cm/°C |
| horizontal | | ASTME831 | 6E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.