برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Water absorption rate | 23℃/sat | ISO 62 | 0.5 % |
23℃/50% RH | ISO 62 | 0.15 % | |
Shrinkage rate | on Tensile Bar,flow | GE Method | 0.7-1 % |
on Tensile Bar,xflow | GE Method | 0.7-1 % |
Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
burning rate | 厚度 1毫米 | FMVSS 302 | 45 mm/min |
UL combustion rating | 94HB Flame Class Rating(3) | UL 94 | 1.5 mm |
94HB Flame Class Rating 2nd value(3) | UL 94 | 3 mm |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
dielectric strength | shorttime,1.0mm | IEC 60243-1 | 18 KV/mm |
in oil,3.2mm | IEC 60243-1 | 17 KV/mm | |
Dielectric loss | 50/60 Hz | IEC 60250 | 0.002 |
1 MHz | IEC 60250 | 0.02 | |
dielectric constant | 50/60 Hz | IEC 60250 | 3.3 |
1 MHz | IEC 60250 | 3.3 | |
Volume resistivity | IEC 60093 | >1.E+14 ohm-cm | |
Surface Resistivity | ROA | IEC 60093 | >1.E+15 Ohm |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
thermal conductance | ISO 8302 | 0.18 W/m-℃ | |
Heat distortion temperature | Be,0.45MPa Edgew 100*10*4 sp=100mm,HDT | ISO 75/Be | 110 °C |
Ae,1.8MPa Edgew 120*10*4 sp=100mm,HDT | ISO 75/Ae | 90 °C | |
Linear coefficient of thermal expansion | flow | ISO 11359-2 | 9E-05 1/℃ |
xflow | ISO 11359-2 | 9E-05 1/℃ | |
Ball pressure test | 75℃/-2℃ | IEC 60695-10-2 | PASSES |
Relative Heat Index (RTI) | Elec | UL 746B | 75 °C |
Mech w/Impact | UL 746B | 75 °C | |
Mech w/o Impact | UL 746B | 75 °C | |
vicat | Rate A/50 | ISO 306 | 150 °C |
Rate B/50 | ISO 306 | 125 °C | |
Rate A/120 | ISO 306 | 127 °C |