برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 2781 | 1.08 g/cm³ |
| MeltViscosity | 190°C,300sec^-1 | ASTM D3835 | 390 Pa·s |
| density | | ASTM D471 | 1.08 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| DurometerHardness | ShoreA,1.90mm,CompressionMolded | ASTM D2240 | 62 |
| Shore hardness | ShoreA,1.90mm,CompressionMolded | ISO 868 | 62 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 7.00 mg |
| Torsion Module | -20°C,1.90mm | ASTM D1043 | 5.50 MPa |
| Torsion Module | 24°C,1.90mm | ASTM D1043 | 2.50 MPa |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| compression set | 24°C,22hr | ASTM D395B | 12 % |
| compression set | 100°C,22hr | ASTM D395B | 54 % |
| Stretch permanent deformation | | ASTM D412 | 6 % |
| tensile strength | 100%Strain,1.90mm2 | ASTM D412 | 3.50 MPa |
| tensile strength | 100%Strain,125°C,1.90mm4 | ASTM D573 | 4.40 MPa |
| tensile strength | 100%Strain,1.90mm2 | ISO 37 | 3.50 MPa |
| tensile strength | 100%Strain,125°C,1.90mm4 | ISO 188 | 4.40 MPa |
| tensile strength | Yield,1.90mm2 | ASTM D412 | 9.70 MPa |
| tensile strength | Yield,125°C,1.90mm4 | ASTM D573 | 11.5 MPa |
| tensile strength | Yield,1.90mm2 | ISO 37 | 9.70 MPa |
| tensile strength | Yield,125°C,1.90mm4 | ISO 188 | 11.5 MPa |
| elongation | Break,125°C,1.90mm4 | ASTM D573 | 410 % |
| elongation | Break,1.90mm2 | ASTM D412 | 470 % |
| elongation | Break,1.90mm2 | ISO 37 | 470 % |
| elongation | Break,125°C,1.90mm4 | ISO 188 | 410 % |
| tear strength | 1.90mm | ASTM D624 | 26.3 kN/m |
| compression set | 24°C,22hr | ISO 815 | 12 % |
| compression set | 100°C,22hr | ISO 815 | 54 % |
| Kappa modulus | -50°C | ASTM D1043 | 68.9 MPa |
| aging | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| volume change | 100°C,168hr,inASTM#1Oil | ISO 1817 | -21 % |
| volume change | 100°C,168hr,inIRM903Oil | ISO 1817 | 23 % |
| volume change | 100°C,168hr,在水中 | ISO 1817 | 6.0 % |
| Hardness change rate in the air | ShoreA,125°C,168hr | ASTM D573 | 4.0 |
| Shore hardness | ShoreA,125°C,168hr | ISO 188 | 4.0 |
| volume change | 27°C,168hr,inReferenceFuelB | ASTM D471 | 19 % |
| volume change | 100°C,168hr,inASTM#1Oil | ASTM D471 | -21 % |
| volume change | 100°C,168hr,inIRM903Oil | ASTM D471 | 23 % |
| volume change | 100°C,168hr,在水中 | ASTM D471 | 6.0 % |
| volume change | 27°C,168hr,inReferenceFuelB | ISO 1817 | 19 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| brittle temperature | | ASTM D746 | -91.0 °C |
| brittle temperature | | ISO 812 | -91.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.