| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | MD:3.20mm | ASTM D955 | 0.49to0.60 % |
| Shrinkage rate | TD:3.20mm | ASTM D955 | 0.56to0.69 % |
| density | | ASTMD792 | 1.10 g/cm³ |
| melt mass-flow rate | 250°C/10.0kg | ASTMD1238 | 16 g/10min |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 106 |
| Rockwell hardness | R-Scale | ISO 2039-2 | 106 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 断裂3 | ASTM D638 | 33.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 30.0 MPa |
| elongation | 断裂3 | ASTM D638 | 25 % |
| elongation | Break | ISO 527-2/50 | 19 % |
| Flexural modulus | --4 | ASTM D790 | 1900 MPa |
| Flexural modulus | --5 | ISO 178 | 2100 MPa |
| bending strength | --4 | ASTM D790 | 61.0 MPa |
| bending strength | --5 | ISO 178 | 65.0 MPa |
| Tensile modulus | --3 | ASTM D638 | 2000 MPa |
| Tensile modulus | -- | ISO 527-2/50 | 2000 MPa |
| tensile strength | 屈服3 | ASTM D638 | 41.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 44.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 28 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 290 J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 130 J/m |
| Impact strength of cantilever beam gap | 23°C6 | ISO 180/1A | 34 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,退火,4.00mm，HDT | ISO 75-2/A | 92.0 °C |
| vicat | | ISO 306/B50 | 104 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 99.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,4.00mm，HDT | ISO 75-2/B | 94.0 °C |
| Heat distortion temperature | 0.45MPa,退火,4.00mm，HDT | ISO 75-2/B | 101 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 90.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,4.00mm，HDT | ISO 75-2/A | 78.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.