impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	--3	ASTM D638	2300	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400	Mpa
tensile strength	Yield4	ASTM D638	65.0	Mpa
	tensile strength	Yield	ISO 527-2/50	65.0	Mpa
		tensile strength	Break4	ASTM D638	55.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0	Mpa
elongation	Yield4	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	4.5	%
		elongation	Break4	ASTM D638	60	%
		elongation	elongation	Break	ISO 527-2/50	25	%
Bending modulus	50.0mmSpan5	ASTM D790	2350	Mpa
Bending modulus	Bending modulus	--6	ISO 178	2200	Mpa
bending strength	--6,7	ISO 178	90.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	95.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.23	W/m/K
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	190	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan10	ISO 75-2/Be	190	°C
Vicat softening temperature	--	ASTM D-596	205	°C
	Vicat softening temperature	--	ISO 306/A50	250	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	200	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	TD:3.20mm	Internal Method	1.1-1.4	%
Water absorption rate	Saturation,23°C	ISO 62	3.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
melt mass-flow rate	280°C/5.0kg	ASTM D1238	13	g/10min
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	13.0	cm3/10min
Shrinkage rate	MD2	Internal Method	1.6-2.0	%
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	1.4-1.7	%
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test	H358/30	ISO 2039-1	85.0	Mpa