Polyolefin, Enhanced TPO POLYTROPE® STR 2030REU-01 NATURAL A SCHULMAN USA

ویژگی‌ها:
thermal performance
مقایسه

برگه داده فنی

	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD：-30to100°C	ASTME831	5.4E-05 cm/cm/°C
UL flame retardant rating	3.2mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	V-0
gloss	60°,3180μm,热塑,光滑	ISO 2813	20to40
HeatSag	149°C,3.20mm	ASTM D3769	0.00 mm
density		ISO 1183	1.31 g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	0.80 g/10min
Shrinkage rate	23°C,24hr,3.18mm	ISO 294-4	0.80to1.2 %
tensile strength	Yield,23°C	ISO 527-2	19.0 MPa
Tensile strain	Break,233°C	ISO 527-2	430 %
Bending modulus	23°C	ISO 178	1930 MPa
Impact strength of cantilever beam gap	-30°C,3.18mm,Injection，Flow	ASTM D256	32 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm,Injection，Flow	ASTM D256	430 J/m
Dart impact	-9°C,TotalEnergy,韧性破坏	ASTM D3763	35.0 J
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	90.6 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.