PP SE 50 E Carmel Olefins Ltd.

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-20°C	ISO 180	5.05.0 kJ/m²
	Impact strength of cantilever beam gap	23°C	ISO 180	35 kJ/m²
		Impact strength of cantilever beam gap	-20°C	ASTM D256	60 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	550 J/m

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ASTM D638	24.0 MPa
tensile strength	tensile strength	Yield	ISO 527-2/50	25.0 MPa
elongation	Yield	ASTM D638	12 %
Tensile strain	Yield	ISO 527-2/50	12 %
Bending modulus		ASTM D790	1150 MPa
Bending modulus	Bending modulus		ISO 178	1200 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	85.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	73.0 °C
Vicat softening temperature		ASTM D15254	150 °C
Vicat softening temperature	Vicat softening temperature		ISO 306/A	150 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	230°C/2.16kg	ASTM D1238	1.3 g/10min
melt mass-flow rate	melt mass-flow rate	230°C/2.16kg	ISO 1133	1.3 g/10min