Fluorelastomer Viton® GBLT-600S The Chemours Company
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.85 g/cm³ | |
| Mooney viscosity | ML1+10,121°C | ASTM D1646 | 65 MU |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | 邵氏A,23°C | ASTM D2240 | 68 |
| 邵氏A,23°C2 | ASTM D2240 | 72 | |
| 邵氏A,23°C3 | ASTM D2240 | 70 | |
| 邵氏A,23°C4 | ASTM D2240 | 72 | |
| 邵氏A,23°C5 | ASTM D2240 | 70 |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| compression set | 200°C,22hr | ASTM D395B | 17 % |
| tensile strength | 23°C6 | ASTM D412 | 0.800 MPa |
| 23°C7 | ASTM D412 | 0.900 MPa | |
| 100%应变,23°C8 | ASTM D412 | 4.20 MPa | |
| 100%应变,23°C9 | ASTM D412 | 5.10 MPa | |
| 100%应变,23°C10 | ASTM D412 | 5.00 MPa | |
| 屈服,23°C12 | ASTM D412 | 12.3 MPa | |
| elongation | 断裂,23°C8 | ASTM D412 | 230 % |
| 断裂,23°C9 | ASTM D412 | 150 % | |
| 断裂,23°C10 | ASTM D412 | 220 % | |
| 断裂,23°C11 | ASTM D412 | 260 % | |
| 断裂,23°C12 | ASTM D412 | 310 % | |
| tensile strength | 100%应变,23°C11 | ASTM D412 | 4.30 MPa |
| 100%应变,23°C12 | ASTM D412 | 3.20 MPa | |
| 屈服,23°C8 | ASTM D412 | 12.7 MPa | |
| 屈服,23°C9 | ASTM D412 | 9.90 MPa | |
| 屈服,23°C10 | ASTM D412 | 16.5 MPa | |
| 屈服,23°C11 | ASTM D412 | 14.1 MPa |
| aging | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| volume change | 23°C,168hr,C级标准燃料 | ASTM D471 | 6.7 % |
| 23°C,168hr,inM15(FuelC/Methanol85/15) | ASTM D471 | 19 % | |
| 23°C,168hr,甲醇 | ASTM D471 | 18 % | |
| 150°C,168hr,在ASTM105油中 | ASTM D471 | 0.80 % |