PA LNP™ THERMOTUF™ VC006 compound SABIC

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	23°C	ASTM D256	210	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C6	ISO 180/1A	21	kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1100	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C6	ISO 180/1U	75	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	32.6	J
Dart impact	Dart impact	--	ISO 6603-2	7.80	J
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Bending modulus	50.0mmSpan4	ASTM D790	15300	MPa
Bending modulus	Bending modulus	--5	ISO 178	15500	MPa
bending strength	--	ISO 178	284	MPa
	bending strength	Yield,50.0mmSpan4	ASTM D790	293	MPa
	bending strength	bending strength	Break,50.0mmSpan4	ASTM D790	286	MPa
Tensile modulus	--2	ASTM D638	20700	MPa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	19300	MPa
tensile strength	Yield3	ASTM D638	197	MPa
	tensile strength	Yield	ISO 527-2/5	193	MPa
	tensile strength	tensile strength	Break	ISO 527-2/5	193	MPa
elongation	Yield3	ASTM D638	2.9	%
	elongation	Yield	ISO 527-2/5	2.9	%
		elongation	Break3	ASTM D638	2.9	%
		elongation	elongation	Break	ISO 527-2/5	2.9	%
tensile strength	Break3	ASTM D638	197	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	261	°C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan7	ISO 75-2/Bf	258	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	252	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan7	ISO 75-2/Af	240	°C
Linear coefficient of thermal expansion	MD:-30to30°C	ASTM D696	3.4E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-30to30°C	ASTM D696	1E-04	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D792	1.21	g/cm³
Shrinkage rate	MD:24hr	ASTM D955	0.25	%
Shrinkage rate	Shrinkage rate	TD:24hr	ASTM D955	1.0	%
Water absorption rate	24hr,50%RH	ASTM D570	0.62	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.95	%

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.