PI, TP JCQ6225A Mitsui Chemicals America, Inc.
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.46 g/cm³ | |
| melt mass-flow rate | 420°C/10.0kg | ASTM D1238 | 33 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.50 % |
| Water absorption rate | 23°C,24hr,60%RH | ASTM D570 | 0.15 % |
| 23°C,24hr | ASTM D570 | 0.30 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 80 J/m |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 23°C | ASTM D638 | 109 MPa |
| elongation | 断裂,23°C | ASTM D638 | 2.0 % |
| Flexural modulus | 23°C | ASTM D790 | 6690 MPa |
| bending strength | 23°C | ASTM D790 | 155 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 238 °C |
| Glass Transition Temperature | ASTME1356 | 240 °C | |
| melting temperature | 388 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.