ABS A120 ASAHI JAPAN
38
- ویژگی‌ها:ضد استاتیک
- گواهی‌نامه‌ها:UL
مقایسهبرگه داده فنی
| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| characteristic | 抗静电 |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | JIS K-7210 | 41 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 断裂 | ASTM D-638 | 46 Mpa |
| elongation at break | ASTM D-638 | 40 % | |
| bending strength | ASTM D-790 | 76 Mpa | |
| Flexural modulus | ASTM D-790 | 2450 Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 108 J/m | |
| tensile strength | ASTM D638/ISO 527 | 40 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2450 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 76 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 108 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 46 % |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 41 g/10min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | ASTM D-1525 | 103 °C | |
| Heat distortion temperature | HDT | ASTM D-648 | 81 °C |
| combustibility | 1/8" | UL 94 | HB |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 81 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 103 ℃（℉） |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.