برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183/B | 1.28 g/cm³ |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 15 g/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.40to0.60 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 960 °C |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 960 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 29 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 4.00mm,InjectionMolded | ISO 527-2/1 | 3950 MPa |
| Tensile modulus | 4.00mm,InjectionMolded | ISO 527-2/50 | 4000 MPa |
| tensile strength | Yield,4.00mm,InjectionMolded | ISO 527-2/50 | 65.0 MPa |
| tensile strength | 断裂,4.00mm,注塑 | ISO 527-2/50 | 50.0 MPa |
| Tensile strain | Yield,4.00mm,InjectionMolded | ISO 527-2/50 | 4.0 % |
| Tensile strain | 断裂,4.00mm,注塑 | ISO 527-2/50 | 9.0 % |
| Flexural modulus | 4.00mm,InjectionMolded | ISO 178 | 3800 MPa |
| bending strength | 4.00mm,InjectionMolded | ISO 178 | 105 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C,InjectionMolded | ISO 180/A | 9.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 2.00mm,1MHz | IEC 60250 | 0.016 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm,SolutionA | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Volume resistivity | 2.00mm | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | >70 kV/mm |
| dielectric constant | 2.00mm,50Hz | IEC 60250 | 3.00 |
| dielectric constant | 2.00mm,1MHz | IEC 60250 | 3.10 |
| Dissipation Factor | 2.00mm,50Hz | IEC 60250 | 8E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 141 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 133 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 139 °C |
| vicat | -- | ISO 306/A120 | 155 °C |
| vicat | -- | ISO 306/B50 | 145 °C |
| Ball pressure temperature | | IEC 60335-1 | >130 °C |
| Linear coefficient of thermal expansion | MD：-40到80°C | ASTM D696 | 1.5E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.