PC+AS(SAN) LNP™ LUBRILOY™ Lexan_WR6300 compound SABIC

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD：3.20mm	内部方法	0.50to0.70 %
density		ASTM D792	1.17 g/cm³
Melt volume flow rate	300°C/2.16kg	ISO 1133	38.0 cm³/10min
Shrinkage rate	MD：3.20mm	内部方法	0.50to0.70 %
density		ASTM D792	1.17 g/cm³
Melt volume flow rate	300°C/2.16kg	ISO 1133	38.0 cm³/10min

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.50mm	UL 94	HB

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	Break	ASTM D638	61.4 MPa
elongation	Break	ASTM D638	160 %
Flexural modulus	50.0mm跨距	ASTM D790	2490 MPa
bending strength	屈服,50.0mm跨距	ASTM D790	96.5 MPa
tensile strength	Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	Break	ASTM D638	61.4 MPa
elongation	Break	ASTM D638	160 %
Flexural modulus	50.0mm跨距	ASTM D790	2490 MPa
bending strength	屈服,50.0mm跨距	ASTM D790	96.5 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
		Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m
			Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	2500 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2500 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat		ASTM D15254	137 °C
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	1.2E-04 cm/cm/°C
Heat distortion temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	134 °C
	Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	117 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	121 °C
RTI Str		UL 746	80.0 °C
Heat distortion temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	134 °C
	Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	117 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	121 °C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
vicat		ASTM D15255	137 °C
Linear coefficient of thermal expansion	MD:-40到40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40到40°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C