EVA UE659 Taiwan Polymer
0
- کاربردها:Compression molding foam hot melt adhesive
مقایسهبرگه داده فنی
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 2 g/10min | |
| density | ASTM D-1505 | 0.947 g/cm3 |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Vinyl acetate content | USIFE | 25 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | ASTM D-2240 | 31 Shore D | |
| elongation | 铸膜成型 | ASTM D-638（ASTM D-882） | 890 % |
| 射出 | ASTM D-638（ASTM D-882） | 236 % | |
| 薄膜MD | ASTM D-638（ASTM D-882） | 290 % | |
| 薄膜TD | ASTM D-638（ASTM D-882） | 680 % | |
| Low temperature brittleness temperature | ASTM D-746 | ＜-76 ℃/F50 | |
| Impact strength of cantilever beam gap | ASTM D-1709 | 444 G/F50 | |
| tensile strength | 铸膜成型，屈服 | ASTM D-638（ASTM D-882） | 212 KG/cm2 |
| 射出，屈服 | ASTM D-638（ASTM D-882） | 114 KG/cm2 | |
| 薄膜MD，屈服 | ASTM D-638（ASTM D-882） | 259 KG/cm2 | |
| 薄膜TD，屈服 | ASTM D-638（ASTM D-882） | 240 KG/cm2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | ASTM D-1525 | 54 ℃ | |
| melting temperature | ASTM D-2117 | 77 ℃ |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.