PP FORMEX® GK-10
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Water absorption rate | Saturation | ASTM D570 | 0.060 % |
| density | ASTM D792 | 1.04 g/cm³ |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | UL 94 | VTM-0 | |
| Limiting Oxygen Index | ASTM D2863 | 29 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| film thickness | 180to330 µm | ||
| tensile strength | MD:屈服 | ASTM D882 | 30.3 MPa |
| TD:屈服 | ASTM D882 | 22.1 MPa | |
| handle | ASTM D2578 | >50 dyne/cm |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 4E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 87 kV/mm | |
| dielectric constant | ASTM D150 | 2.30 | |
| Dissipation Factor | ASTM D150 | 1.9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | ASTM D3638 | PLC 0 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | mm/min |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 sec |
| dielectric strength | ASTM D149 | 22000 V |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| RTI | UL 746 | 115 °C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTM D648 | 121 °C |
| RTI Elec | UL 746 | 115 °C |