PA6 H8202NLB AdvanSix
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.3 % |
| Water absorption rate | 24hr | ASTM D570 | 1.6 % |
| Saturation | ASTM D570 | 9.5 % | |
| Equilibrium | ASTM D570 | 2.7 % | |
| Extractable content | 内部方法 | <0.8 % | |
| water content | ASTM D6869 | <0.10 % | |
| relative viscosity | 2.61 | ||
| Viscosity FAV | ASTM D789 | 46.0to52.0 | |
| density | ASTM D792 | 1.13 g/cm³ | |
| melt mass-flow rate | 235°C/1.0kg | ASTM D1238 | 9.8 g/10min |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 119 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | 23°C | ASTM D638 | 2850 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 79.0 MPa |
| elongation | 屈服,23°C | ASTM D638 | 4.0 % |
| 断裂,23°C | ASTM D638 | 55 % | |
| Flexural modulus | 23°C | ASTM D790 | 3010 MPa |
| bending strength | 23°C | ASTM D790 | 110 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 50 J/m |
| 23°C | ASTM D256 | 60 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 178 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 65.0 °C | |
| melting temperature | ASTM D3418 | 220 °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 8.3E-05 cm/cm/°C |